Multilayer heat shrinkable film comprising styrene polymer or a blend of styrene polymers

ABSTRACT

The present invention provides a multilayer heat shrinkable film incorporating an oxygen barrier material and layer comprising a styrene polymer or blend of styrene polymers, where the shrinkage of the film in at least one of MD, TD is at least 30% at 90° C. The invention is further directed to a method of manufacturing a bag from said multilayer heat shrinkable film.

CROSS-REFERENCES

This application is a continuation application of U.S. patent application Ser. No. 11/063,029, filed Feb. 22, 2005, the contents of which are incorporated herein by reference in their entirety.

FIELD OF THE INVENTION

This invention relates to multilayer heat shrinkable films.

This invention has particular application to such films for use in packaging or foods such as meat, poultry and the like. However, it is envisaged that films in accordance with the present invention may find use in other packaging applications such as packaging for curable putties and sealants and for various types of respiring and non respiring cheese.

BACKGROUND OF THE INVENTION

Primal meat cuts are generally smaller than a side of beef, but larger than the ultimate cut sold to the retail consumer. Primal cuts are prepared at the slaughter house and shipped to retail meat stores or restaurants where they are butchered into smaller cuts of meat commonly referred to as sub-primal meat cuts. Sub-primal cuts, however, may also be prepared at the slaughterhouse.

Primal and sub-primal cuts are packaged to minimize air (i.e. oxygen) exposure and prevent meat spoilage and discoloration during shipping and handling. One common way to package primal and sub-primal cuts and protect them from the adverse effects of air is to shrink package the cuts in a film having good oxygen barrier properties. For example, a multilayer film having a barrier layer containing polyvinylidene chloride (PVDC) is a well-known packaging material. PVDC is known to have excellent oxygen barrier properties. The other layers of the multilayer film function to protect the PVDC layer and provide the requisite low temperature and abrasion resistance properties, which the PVDC layer lacks. There are other types of biaxially oriented heat shrinkable multilayer films, which do not require oxygen barrier properties, for example films to be used for shrink wrapping poultry.

Shrinkage properties may be produced in a film by biaxially stretching the film in the machine and transverse direction. The resulting film will heat shrink within a specified range of percentages such as from about 20 to about 50 percent at about 90° C. Preferably the shrinkage should be more than 30 percent in at least one of machine and transverse directions at 90° C.

A multilayer heat shrinkable film may also be formed into packaging bags. Bags are generally made by transversely sealing a tubular stock of multilayer film and cutting or splitting the tube, or by superimposing flat sheets of multilayer film and sealing on three sides, or by end folding flat sheets and sealing the two sides. A common type of seal used in manufacturing bags is a hot bar seal. The adjacent thermoplastic layers, referred to as the inner layers, are sealed together by application of heat and pressure across the area to be sealed, using contact with opposing bars of which at least one is heated to cause the adjacent layers to fusion bond. Bags manufactured from a tube stock generally require one hot bar seal transverse to the tube. This seal is also referred to as a bottom seal. Once the bottom seal is applied, the tube stock is transversely cut to form the mouth of the bag. The strength of seals may be measured by determining the time for a seal to fail when under certain conditions. For example, the seal is immersed in hot water at 95° C. and the hot water seal strength (“HWSS”) may be measured by a test such as that described as the “restrained shrinkage-seal strength test” in Funderburk et al U.S. Pat. No. 3,900,635.

Once meat or poultry is inserted into the bag, the package is evacuated and the bag mouth must be sealed. At one time, the standard method for sealing a bag was to fasten a clip around the mouth of the bag. Today, impulse heat sealing techniques are employed to seal the bag mouth. In general, a bag mouth is impulse sealed by application of heat and pressure using opposing bars. At least one of the bars has a covered wire or ribbon through which electric current is passed for a very brief time period (hence the name “impulse”) to cause the adjacent film layers to fusion bond. Following the impulse of heat the bars are cooled while continuing to hold the bag inner surfaces together to achieve adequate seal strength.

Irradiation of a multilayer film causes the various irradiated layers in the film to cross-link. Under controlled conditions, cross-linking by irradiation not only provides a higher temperature impulse heat sealing range, but also enhances the puncture resistance of the film. Under controlled conditions, polymeric multilayer films can be irradiated to produce a cross-linked product having greater puncture resistance characteristics and other enhancements.

Three basic requirements of a commercial shrinkable multilayer film are as follows

-   -   1. Excellent optical properties, such as low haze and high         gloss, both before and after shrinkage. This is important for         the better aesthetic presentation of the product.     -   2. Shrinkage at least as high as 30 percent in at least one         direction at temperatures about 90° C. This also contributes to         better presentation of the product to the consumer (in super         markets).     -   3. Easy bag making of the product (reduced scrap during bag         making). This is more easily achievable when the film is         comparatively stiff.

Prior art films typically used may have low haze and high gloss in unshrunk configuration, but much worse optical properties after shrinking. Alternatively, they may keep their optical properties after shrinkage, but do not shrink enough for an acceptable product presentation.

Therefore, it is an object of the present invention to provide a multilayer heat shrinkable film, which optimizes the clarity-shrinkage behaviour. It is a further object of the present invention to render the bag making process more efficient than with existing films.

These objects are solved by the subject-matter of the independent claims. Preferred embodiments are set forth in the dependent claims.

SUMMARY OF THE INVENTION

This invention in one aspect resides broadly in a multilayer heat shrinkable film including a layer of styrene polymer or a blend of styrene polymers and an oxygen barrier polymer layer. The film shrinks at least 30% in at least one of machine and transverse directions by measuring unrestrained shrink of the stretched film at 90° C. for five seconds, or equivalent shrinkage thereof.

As used herein, the term “polymer” refers to the product of a polymerization reaction and is inclusive of homopolymers, copolymers, terpolymers etc.

As used herein, the term “homopolymer” is used with reference to a polymer resulting from the polymerization of a single monomer.

As used herein the term “copolymer” refers to polymers formed by the polymerization reaction of at least two different monomers.

As used herein, the term “polypropylene” refers to any polymer comprising propylene polymerization units regardless of whether the polymer is a homopolymer or a copolymer and further includes blends of such homopolymers and copolymers.

As used herein the term “ethylene propylene copolymer” refers to polypropylene copolymerized with ethylene monomer.

As used herein the phrase “ethylene alpha-olefin copolymer” refers to such heterogeneous materials as linear low density polyethylene (LLDPE), linear medium density polyethylene (LMDPE) and very low and ultra low density polyethylene (VLDPE and ULDPE), as well as homogeneous polymers such as TAFMER™ supplied by Mitsui Petrochemical corporation and metallocene catalysed polymers such as Exact materials supplied by Exxon. Other ethylene alpha olefin copolymers such as the long chain branched homogeneous alpha olefin copolymers available from Dow Chemical Company, known as Affinity resins, are also included in the present invention. Homogeneous ethylene alpha olefin copolymers with a density less than about 0.905 are generally called plastomers.

As used herein “EVOH” refers to ethylene vinyl alcohol copolymer.

As used herein “PVDC” refers to vinylidene chloride homopolyers and copolymers.

As used herein, the term “polyamide” refers to high molecular weight polymers having amide linkages along the molecular chain and refers more specifically to synthetic polyamides such as nylons.

As used herein, the term “barrier” is used with reference to the ability of films to serve as barrier to oxygen or other gases.

As used herein, the term “oriented” refers to a polymer containing material which has been stretched at an elevated temperature, followed by being “set” in the stretched configuration by cooling the material while substantially retaining the stretched dimensions.

As used herein, the phrase “heat shrinkable”, “heat shrink” and the like, refer to the tendency of a film, especially an oriented film, to shrink upon the application of heat.

As used herein, the phrase “ethylene vinyl acetate” or EVA, refers to a copolymer formed from ethylene and vinyl acetate monomers, wherein the ethylene derived units in the copolymer are present in major amounts, preferably between about 60 to about 98 percent, while the vinyl acetate derived units in the copolymer are present in minor amounts, preferably between about 2 and 40 percent.

As used herein, the phrase “ethylene methyl acrylate”, or EMA, refers to a copolymer formed from ethylene and methyl acrylate monomers, wherein the ethylene derived units in the copolymer are present in major amounts, preferably between about 60 to about 98 percent, while the methyl acrylate derived units in the copolymer are present in minor amounts, preferably between about 2 and 40 percent.

As used herein, the phrase “cycloolefin copolymer” refers to a copolymer composed of ethylene units and/or of units comprising an alpha olefin with a cyclic, bicyclic or multicyclic olefin. Preferably the COC is a copolymer of ethylene and norbornene.

The styrene content in the polymers used in the present invention is preferably more than 50 wt. % of styrene in the styrene copolymer. Preferably, more than 60 wt. %, further preferably more than 70%, more than 80% or even more than 90% by weight of styrene in the styrene copolymer is used. In another preferred embodiment a styrene homopolymer is used.

As used herein the term “ionomer” is a copolymer of ethylene with an ethylenically unsaturated acidic monomer, for instance acrylic or methacrylic acid. The ionomer is preferably in its ionised form, the neutralizing cation being any suitable metal. A well known ionomer material is Surlyn from Dupont.

DETAILED DESCRIPTION OF THE INVENTION

According to a first and main aspect, the invention provides a multilayer heat shrinkable film comprising at least

-   -   a) a layer comprising an oxygen barrier material,     -   b) a layer comprising a styrene polymer or a blend of styrene         polymers,

where the shrinkage of the film in at least one of MD, TD (machine direction, transverse direction) is at least or more than 30% at 90° C.

In one preferred embodiment of the invention, the layer of the styrene polymer or blend of styrene polymers is the outer layer of the structure, being exposed to the environment.

In a further embodiment, between the layer of the styrene polymer or blend of styrene polymers and the barrier layer there is a bonding layer which may include ethylene ester copolymers or ethylene alpha olefin copolymers.

Additionally, the multilayer heat shrinkable film of the invention may comprise a heat sealable inner layer. The inner layer may be made of a heat sealable thermoplastic polymer or polymer blend. The heat sealable inner layer may be of any material conventionally used for its heat sealing capability. Heat sealable thermoplastic polymers are recognized by those skilled in the art as being capable of heat sealing to themselves at a variety of time, pressure and temperature conditions. For example, at a given pressure either a relatively high temperature may be applied briefly or a lower temperature may be applied for a longer period of time to obtain similarly suitable seals. It is to be appreciated that persons skilled in the art will be able to select sealing parameters such as temperature, pressure and time of application that depend upon such factors as the type of heat sealing equipment used. The term “inner layer” generally relates to that side of the multilayer heat shrinkable film, which is not exposed to the environment in a given product form (e.g. bag), but the good to be packaged.

This inner sealing layer may for instance be an alpha olefin copolymer or a blend of alpha olefin copolymers, e.g. a VLDPE, EVA, plastomer or a blend thereof. Alternatively, a styrene polymer or a blend of styrene polymers may also be used as the inner heat sealing layer. In another embodiment, a cycloolefin copolymer or a blend of cycloolefin copolymer and alpha olefin copolymer may be the inner sealing layer.

Suitable polymers and copolymers may include alpha olefins such as members of the polyethylene family such as linear low-density polyethylene (LLDPE); very low-density polyethylene sometimes referred to as ultra low-density polyethylene (VLDPE and ULDPE respectively), plastomers or blends thereof. Still other suitable thermoplastic polymers as the heat sealable inner layer include polypropylene, ethylene-propylene copolymer or an ionomer. It is to be understood however that the thermoplastic polymers mentioned herein are not intended to be an exhaustive list, but merely exemplary.

In a preferred embodiment of the invention, the outer layer (directly exposed to the environment) comprises a styrene copolymer in a blend with a slip agent.

Preferred styrene polymers are polystyrene homopolymer, SBC (styrene butadiene copolymers), SBS copolymers, SIS copolymers, SEBS copolymers, Ethylene Styrene interpolymers and blends thereof. Suitable materials are K RESIN from Chevron Philips Chemical, FINACLEAR from Atofina and Styrolux from BASF. A preferred styrene homopolymer is STYRON from Dow. In one preferred embodiment, the styrene content of the material is more than 50% by weight. This increases the stiffness of the material, thus making it more easy to convert.

One functional requirement of the barrier layer may be that together with the other layers, the oxygen transmission rate through the entire multilayer film may be below about 20 cc/1 m²/24 hrs/atm, measured at 23 C, 75% RH. This is to avoid spoilage of certain food products, for example meat enclosed in the multilayer film package due to oxygen passage from the environment through the film wall. This requirement may be satisfied by numerous well-known barrier layer materials. For example, these may include certain of the polyamides (Nylon), hydrolyzed ethylene vinyl acetate copolymer (EVOH) and preferably a vinylidene copolymer. Vinylidene chloride-vinyl chloride (PVDC) is a commonly used copolymer but vinylidene chloride-methyl acrylate copolymer (MA-VDC) may also be used.

The thickness of the heat sealable inner thermoplastic first layer may be between about 0.4 mils and about 2.0 mils. Thinner layers may not perform the described functions while thicker layers may not appreciably improve processability of the film and may reduce total film performance.

The barrier layer thickness may be between about 0.1 mils to about 0.5 mils. Thinner barrier layers may not perform the intended functions and thicker layers do not appreciably improve performance.

Regardless of the structure of the film, one or more film additives may be incorporated, such as slip agents, antiblock agents, colorants, odor inhibitors, oxygen inhibitors etc. The skilled in the art technician can be well aware of these additives.

While the composition of the film may eliminate the need for irradiation of the multilayer film, it is to be understood that the multilayer heat shrinkable film in accordance with the invention may be irradiated to further enhance puncture and temperature resistance.

According to a preferred embodiment, the multilayer heat shrinkable film of the invention comprises the following components:

a) an outer layer of a styrene amorphous copolymer

b) an adjacent (bonding) layer of a blend of EMA copolymer, EVA copolymer and metallocene LLDPE

c) a barrier core layer comprising PVDC copolymer

d) an adjacent (bonding) layer of EVA copolymer or EMA copolymer, EVA copolymer and metallocene LLDPE

e) an inner sealing layer comprising EVA, VLDPE, or a plastomer or a blend thereof.

The heat shrinkable multilayer film in accordance with the present invention may be in the form of a tubular article or flat sheets. The multilayer film may be formed into bags useful for the packaging of meats. The multilayer film may be especially useful for those bags manufactured by hot bar or impulse sealing, and after meat is inserted therein, impulse heat sealing may be used to seal the mouth.

One end of the bag may be heat sealed by adhesion between contiguous inner layer surfaces in a direction transverse to the oppositely located sidewalls of the bag. The mouth end of the bag may be impulse heat sealable by fusion bonding between contiguous inner layer surfaces after filling the bag with food.

A bag from the multilayer film may be manufactured such that the inner layer forms the inside portion of the bag while the outer layer forms the outside portion of the bag. Accordingly, the inner layer of the tubular multilayer film may be the heat sealable layer, which is easily sealed by hot bar sealing. Moreover, because of the latter, the mouth of the bag may be more easily sealed by impulse heat sealing.

Thus, according to a second aspect, the invention is directed to a method for manufacturing a bag from a multilayer shrinkable film as defined above, comprising the steps of:

-   -   a) forming a bag, in which the inner layer of the multilayer         heat shrinkable film as defined herein forms the inside portion         of the bag while its outer layer forms the outside portion of         the bag,     -   b) inserting a good to be packaged into the bag, and     -   c) sealing the bag by hot bar or impulse sealing.

Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention pertains. All references mentioned herein are incorporated by reference in their entirety. In case of conflict, the present specification, including definitions, will control. In addition, the examples are illustrative only and not intended to be limiting.

EXAMPLES

In this series of tests, bags of the same size (400 mm long×230 mm wide) and of 60 micron thickness were fabricated from films comprising a heat sealable thermoplastic inner layer, an adjacent layer adhered on one side to the sealable inner layer, an oxygen barrier layer, an adjacent layer and an outer layer. The core layer in most tests was a vinylidene chloride copolymer type oxygen barrier. The film was the biaxially oriented heat shrinkable type, prepared by the double or trapped bubble method as broadly described in the aforementioned Palkhe U.S. Pat. No. 3,456,044. In particular, all layers were simultaneously coextruded.

Certain physical properties of bags were measured by either of the test procedures discussed below.

Shrinkage values were obtained by measuring unrestrained shrink of the stretched film at 90° C. for five seconds. Four test specimens were cut from a given sample of the oriented film to be tested. The specimens were cut to 10 cm in the machine direction by 10 cm. in the transverse direction. Each specimen was completely immersed for 5 seconds in a 90° C. water bath. The distance between the ends of the shrunken specimen was measured. The difference in the measured distance for the shrunken specimen and the original 10 cm was multiplied by ten to obtain the percent of shrinkage for the specimen. The shrinkage for the four specimens was averaged for the MD shrinkage values of the given film sample, and the shrinkage for the four specimens was averaged for the TD shrinkage value.

The tensile modulus compared below has been measured according to ASTM D 882 with an Instron testing device. The optical properties were tested according to ASTM D1003(haze) and BS 2782(gloss).

The bag making testing was done with a use of a commercial bag making machine.

Example 1

A heat shrinkable multilayer film was produced having:

a) an outer layer of a styrene amorphous copolymer

b) an adjacent layer of a blend of EMA copolymer, EVA copolymer and metallocene LLDPE

c) a barrier core layer

d) an adjacent layer of EVA copolymer

e) an inner sealing layer

More specifically

Outer layer: 98% S1+2% slip masterbatch, 12% of the total structure

Adjacent layer 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 19% of the total structure

Barrier layer: PVDC copolymer, 11% of the total structure

Adjacent layer: 100% E1, 12% of the total structure

Inner sealing layer: 20% E1+10% E2+32% P1+30% V1+8% ADDITIVES, 46% of the total structure.

Example 2

A heat shrinkable multilayer film was produced having:

a) an outer layer of a styrene amorphous copolymer

b) an adjacent layer of a blend of EMA copolymer, EVA copolymer and metallocene LLDPE

c) a barrier core layer

d) an adjacent layer of EMA copolymer, EVA copolymer and metallocene LLDPE

e) an inner sealing layer

More specifically

Outer layer: 98% S1+2% slip masterbatch, 12% of the total structure

Adjacent layer 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 19% of the total structure

Barrier layer: PVDC copolymer, 11% of the total structure

Adjacent layer: 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 12% of the total structure

Inner sealing layer: 20% E1+10% E2+32% P1+30% V1+8% ADDITIVES, 46% of the total structure

Comparative Example 3

As a comparative example, we use a commercial product of FLEXOPACK under the name FMX containing no styrene.

Example 4

Outer layer: 98% S1+2% slip masterbatch, 12% of the total structure

Adjacent layer 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 19% of the total structure

Barrier layer: PVDC copolymer, 11% of the total structure

Adjacent layer: 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 12% of the total structure

Inner sealing layer: 20% E1+10% E2+32% P1+30% P2+8% ADDITIVES, 46% of the total structure

Example 5

Outer layer: 98% S1+2% slip masterbatch, 12% of the total structure

Adjacent layer 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 19% of the total structure

Barrier layer: PVDC copolymer, 11% of the total structure

Adjacent layer: 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 12% of the total structure

Inner sealing layer: 30% E1+62% P2+8% ADDITIVES, 46% of the total structure

Example 6

Outer layer: 98% S1+2% slip masterbatch, 12% of the total structure

Adjacent layer 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 19% of the total structure

Barrier layer: PVDC copolymer, 11% of the total structure

Adjacent layer: 15% M1+15% M2+45% E1+20% LL1+5% ADDITIVES, 12% of the total structure

Inner sealing layer: 30% E1+42% P2+20% C1+8% ADDITIVES, 46% of the total structure

The films were e-beam radiated with a dose of 4 MRAD.

TABLE 1 SHRINKAGE COMPARISONS SHRINK- SHRINK- SHRINK- SHRINK- AGE AGE AGE AGE SAMPLE 80 C. 85 C. 90 C. 95 C. NOTES EXAMPLE 1 28/28 39/37 50/48 55/46 EXAMPLE 2 30/30 38/35 50/47 55/47 EXAMPLE 3 30/32 38/37 49/45 55/49 EXAMPLE 4 31/31 42/40 50/50 57/52 EXAMPLE 5 27/28 37/37 50/45 55/47 EXAMPLE 6 32/32 44/44 50/50 57/55

According to TABLE 1, there is practically no difference in the comparison of shrinkage between the three different materials.

In the following table the optical property comparisons are explained.

TABLE 2 HAZE AFTER SAMPLE HAZE GLOSS SHRINKAGE NOTES EXAMPLE 1 8.2 92 30 Excellent clarity after shrink onto product EXAMPLE 2 9 92 36 Excellent clarity after shrink onto product EXAMPLE 3 10.5 81 40 Good clarity after shrink onto product EXAMPLE 4 7.5 97 25 Excellent clarity after shrink onto product EXAMPLE 5 8 95 27 Excellent clarity after shrink onto product EXAMPLE 6 11.5 94 45 Excellent clarity after shrink onto product

Measurement of tensile modulus has been also carried out, according to ASTM D 882.

TABLE 3 TENSILE NOTES MODULUS DURING BAG SAMPLE MD/TD NOTES MAKING EXAMPLE 1 210/195 stiff Very easy to convert EXAMPLE 2 239/209 stiff Very easy to convert EXAMPLE 3 173/175 soft Convertible only with reduced machine speed. Blocks during bag making. EXAMPLE 4 205/190 Easy to convert EXAMPLE 5 230/225 Very easy to convert EXAMPLE 6 250/250 Very easy to convert

The resins used are explained in table 4.

TABLE 4 Melt Den- Melting Index sity point Type Description Manufacturer g/10 min g/cm³ ° C. E1 EVA Dupont 3135 X 0.35 0.93 95 E2 EVA 1005 VN2 0.40 0.928 102 V1 VLDPE Dow Attane 1.00 0.912 122 SL 4100 P1 Plastomer Dow Affinity 1.0 0.885 74 VP 8770 PB1 Polybutylene Shell 8640 2 118 LL1 LLDPE Atofina M3410 1 0.934 123 S1 SB DK13 10 1.01 COPOLYMER M1 EMA Atofina 2-3.5 0.95 61 copolymer LOTRYL 29MAO3 M2 EMA Atofina 0.5 0.94 70 copolymer LOTRYL 24MA005 P2 Plastomer Dow Affinity 1 0.902 100 PL 1880 C1 Cycloolefin Ticona Topas 1.02 copolymer 8007 

1. A five-layer heat shrinkable oxygen barrier film comprising: a) an outer layer consisting essentially of a styrene amorphous copolymer; b) a first bonding layer adjacent to the outer layer, the first bonding layer consisting essentially of a blend of ethylene methyl acrylate copolymer, ethylene vinyl acetate copolymer, and metallocene-catalyzed linear low density polyethylene; c) a barrier core layer adjacent to the first bonding layer, the barrier core layer consisting essentially of an oxygen barrier polymer; d) a second bonding layer adjacent to the barrier core layer, the second bonding layer consisting essentially of a blend of ethylene methyl acrylate copolymer, ethylene vinyl acetate copolymer, and metallocene-catalyzed linear low density polyethylene; and e) an inner sealing layer adjacent to the second bonding layer, the inner sealing selected from the group consisting of an ethylene vinyl acetate copolymer, a very low density polyethylene, a plastomer, and blends thereof, wherein the heat shrinkable, oxygen barrier film has a shrinkage in at least one direction of at least 30% at a temperature of 90° C., and an oxygen transmission rate less than about 20 cc/liter-m2/24 hrs/atm, measured at 23° C. and 75% relative humidity.
 2. The film as recited in claim 1, wherein the styrene amorphous copolymer has a styrene content exceeding 50% by weight of the copolymer.
 3. The film as recited in claim 1, wherein the styrene amorphous copolymer comprises styrene and butadiene.
 4. The film as recited in claim 1, wherein the styrene amorphous copolymer comprises styrene and isoprene.
 5. The film as recited in claim 1, wherein the styrene amorphous copolymer comprises styrene and ethylene.
 6. The film as recited in claim 1, wherein the oxygen barrier polymer comprises a vinylidene chloride copolymer.
 7. The film as recited in claim 6, wherein the vinylidene chloride copolymer comprises vinylidene chloride and vinyl chloride.
 8. The film as recited in claim 6, wherein the vinylidene chloride copolymer comprises vinylidene chloride and methyl acrylate.
 9. The film as recited in claim 1, wherein the oxygen barrier polymer comprises a polyamide.
 10. The film as recited in claim 1, wherein the oxygen barrier polymer comprises ethylene vinyl alcohol.
 11. The film as recited in claim 1, wherein the inner sealing layer comprises a plastomer having a density less than about 0.905 grams/cm3.
 12. The film as recited in claim 11, wherein the plastomer is metallocene-catalyzed.
 13. The film as recited in claim 11, wherein the inner sealing layer further comprises an ethylene vinyl acetate copolymer.
 14. The film as recited in claim 11, wherein the inner sealing layer further comprises very low density polyethylene.
 15. The film as recited in claim 1, wherein the film is formed as a tubular article.
 16. The film as recited in claim 1, wherein the film is formed as a flat sheet.
 17. The film as recited in claim 1, wherein the film is formed as a bag.
 18. The film as recited in claim 1, wherein the film is irradiated.
 19. The film as recited in claim 1, wherein the barrier core layer has a thickness between about 0.1 mils and about 0.5 mils.
 20. The film as recited in claim 1, wherein the inner sealing layer has a thickness between about 0.4 mils and about 2.0 mils.
 21. The film as recited in claim 1, having a shrinkage of at least 30% in at least two directions at a temperature of 90° C.
 22. A multi-layer film comprising: an abuse layer comprising styrene-butadiene block copolymer; a first tie layer adjacent the abuse layer comprising ethylene vinyl acetate; a gas barrier layer adjacent the first tie layer comprising polyvinylidene chloride; a second tie layer adjacent the gas barrier layer comprising ethylene vinyl acetate; and a sealant layer adjacent the second tie layer comprising a metallocene-catalyzed polymer, wherein the metallocene-catalyzed polymer is at least one of selected from linear low density polyethylene and or ultra low density polyethylene, and wherein the film is heat shrinkable and shrinks at temperatures between about 75° C. and about 90° C.
 23. The film as recited in claim 22, wherein the thickness of the abuse layer comprises about 11% to about 12% of total film thickness.
 24. The film as recited in claim 23, wherein the thickness of the first tie layer comprises about 5% to about 15%, the thickness of the gas barrier layer comprises about 5% to about 15%, the thickness of the second tie layer comprises about 35% to about 55%, and the thickness of the sealant layer comprises about 5% to about 15%, each based on the total film thickness.
 25. The film as recited in claim 24, wherein the abuse layer is about 12%, the first tie layer is about 14%, the gas barrier layer is about 9%, the second tie layer is about 54%, and the sealant layer is about 11%, based on total film thickness.
 26. The film as recited in claim 22, wherein the film has a total thickness of about 1.5 mils to about 2.5 mils.
 27. The film as recited in claim 22, wherein the styrene-butadiene block copolymer comprises about 75 wt % polystyrene based on the total weight of the polystyrene and butadiene.
 28. The film as recited in claim 22, wherein the first tie layer and the second tie layer, independently, have a density of between about 0.92 g/cm³ and about 0.98 g/cm³.
 29. The film as recited in claim 28, wherein the density of each tie layer is about 0.942 g/cm³.
 30. The film as recited in claim 22, wherein the metallocene-catalyzed sealant comprises metallocene-catalyzed linear low density polyethylene. 